1100 H14 aluminum is a high-purity commercial alloy known for its reliable corrosion resistance, strong thermal conductivity, and easy workability. It performs well in forming, bending, and general fabrication. If you need stable quality and a consistent supply, feel free to contact us for a customized quotation.
| Product Name | 1100 h14 |
| Standard | UNS A9100,QQA 250/1 |
| Thickness | 0.008″ – 0.125″ |
| Width | 600mm-2600mm |
| Length | 400mm-1600mm |
| Surface Treatment | color coated |
| MOQ | 1 TON |
| Aluminum (Al) | 99.00% |
| Silicon (Si) | 0.45% |
| Copper (Cu) | 0.05–0.20% |
| Magnesium (Mg) | — |
| Zinc (Zn) | 0.01% |
| Manganese (Mn) | 0.035% |
| Titanium (Ti) | — |
| Vanadium (V) | 0.05% |
| Iron (Fe) | 0.35% |
| Property | 1100 H14 | 1100 H24 |
| Typical Tensile Strength (UTS) | 95–130 MPa | 90–140 MPa |
| Typical Yield Strength (Rp0.2) | 95–110 MPa | Medium (lower than full-hard, higher than O temper) |
| Typical Elongation (%) | 6–12% | Medium (less than O temper but more than H18) |
| Workability | Good formability; suitable for general bending and light drawing | Balanced option; easier to process than H18 but less ductile than O |
| Characteristics | Most widely used commercial temper with balanced strength and ductility | Offers a middle ground between strength and formability; suitable for moderate forming operations |