5052 aluminum tube is an Al-Mg series rust-resistant aluminum alloy with outstanding corrosion resistance, weldability, and cold working properties. Its tensile strength reaches 170-305 MPa and it has high fatigue strength and oxidation resistance. 5052 aluminum tube is widely used in the aerospace industry to manufacture aircraft oil pipes and ship sheet metal parts. It is an ideal high-rust and oxidation-resistant metal material.
| Alloy | 5052 |
| Temper | O , H32, H34, H36, H38，H112 |
| Type | Extruded, Cold Drawn, Seamless |
| OD | 3 mm – 200 mm (0.125″ – 8″) |
| WT | 0.45 mm – 11.5 mm (0.018″ – 0.45″) |
| Small diameter, thin wall type | OD 3–50mm, wall thickness 0.5–2.0mm |
| Medium diameter, medium wall type | OD 50–150mm, wall thickness 2.0–6.0mm |
| Large diameter, thick wall type | OD up to 200mm and above, wall thickness 6–11mm |
| Length | Standard length 2500mm |
| Surface Finish | Mill Finish, Anodized, Powder Coated, Polished, Brushed[👉Click to view surface treatment details] |
| Standards | ASTM B210, ASTM B241, ASTM B483, AMS 4070, JIS H4000, EN 573-3, EN 754 [👉Click to view details] |
| Equivalent Name | UNS A95052, AlMg2.5, 3.3523, A-G2.5 |
| Processing Services | CNC Cutting, Drilling, Etching, Bending, Welding [👉Click to view processing services] |
| Delivery Conditions | Packaged in PE wrap + wooden cases |
| Applications | Marine structures, Fuel lines, HVAC systems, Architectural structures, Automotive, Aerospace, Rivets, Hydraulic tubing |
| Type | OD(in） | TH（in） | ID(in) |
| 5052 O Extruded Aluminum Tube 0.25(OD)x0.020(WT) | 0.25 | 0.02 | 0.21 |
| 5052 O Extruded Aluminum Tube 0.25(OD)x0.042(WT) | 0.25 | 0.042 | 0.166 |
| 5052 O Extruded Aluminum Tube 0.5(OD)x0.035(WT) | 0.5 | 0.035 | 0.43 |
| 5052 O Extruded Aluminum Tube 0.75(OD)x0.065(WT) | 0.75 | 0.065 | 0.62 |
| 5052 O Extruded Aluminum Tube 1.0(OD)x0.035(WT) | 1 | 0.035 | 0.93 |
| 5052 O Extruded Aluminum Tube 1.5(OD)x0.065(WT) | 1.5 | 0.065 | 1.37 |
| 5052 O Extruded Aluminum Tube 2.0(OD)x0.050(WT) | 2 | 0.05 | 1.9 |
| 5052 O Extruded Aluminum Tube 3.0(OD)x0.090(WT) | 3 | 0.09 | 2.82 |
| 5052 O Extruded Aluminum Tube 4.0(OD)x0.125(WT) | 4 | 0.125 | 3.75 |
| 5052 O Extruded Aluminum Tube 6.0(OD)x0.187(WT) | 6 | 0.187 | 5.63 |
| 5052 Cold Draw Aluminum Tube 0.125(OD)x0.020(WT) | 0.125 | 0.02 | 0.085 |
| 5052 Cold Draw Aluminum Tube 0.25(OD)x0.020(WT) | 0.25 | 0.02 | 0.21 |
| 5052 Cold Draw Aluminum Tube 0.25(OD)x0.035(WT) | 0.25 | 0.035 | 0.18 |
| 5052 Cold Draw Aluminum Tube 0.5(OD)x0.035(WT) | 0.5 | 0.035 | 0.43 |
| 5052 Cold Draw Aluminum Tube 0.75(OD)x0.035(WT) | 0.75 | 0.035 | 0.68 |
| 5052 Cold Draw Aluminum Tube 1.0(OD)x0.050(WT) | 1 | 0.05 | 0.9 |
| 5052 Cold Draw Aluminum Tube 1.25(OD)x0.065(WT) | 1.25 | 0.065 | 1.12 |
| 5052 Cold Draw Aluminum Tube 1.5(OD)x0.065(WT) | 1.5 | 0.065 | 1.37 |
| 5052 Cold Draw Aluminum Tube 2.0(OD)x0.090(WT) | 2 | 0.09 | 1.82 |
| 5052 Cold Draw Aluminum Tube 2.5(OD)x0.095(WT) | 2.5 | 0.095 | 2.31 |
| 5052 Cold Draw Aluminum Tube 3.0(OD)x0.125(WT) | 3 | 0.125 | 2.75 |
| 5052 Cold Draw Aluminum Tube 4.0(OD)x0.125(WT) | 4 | 0.125 | 3.75 |
| 5052 SeamlessAluminum Tube 0.25(OD)x0.035(WT) | 0.25 | 0.035 | 0.18 |
| 5052 SeamlessAluminum Tube 0.375(OD)x0.035(WT) | 0.375 | 0.035 | 0.305 |
| 5052 SeamlessAluminum Tube 0.5(OD)x0.035(WT) | 0.5 | 0.035 | 0.43 |
| 5052 SeamlessAluminum Tube 0.75(OD)x0.049(WT) | 0.75 | 0.049 | 0.652 |
| 5052 SeamlessAluminum Tube 1.0(OD)x0.065(WT) | 1 | 0.065 | 0.87 |
| 5052 SeamlessAluminum Tube 1.25(OD)x0.065(WT) | 1.25 | 0.065 | 1.12 |
| 5052 SeamlessAluminum Tube 1.5(OD)x0.083(WT) | 1.5 | 0.083 | 1.334 |
| 5052 SeamlessAluminum Tube 2.0(OD)x0.083(WT) | 2 | 0.083 | 1.834 |
| 5052 SeamlessAluminum Tube 2.5(OD)x0.095(WT) | 2.5 | 0.095 | 2.31 |
| 5052 SeamlessAluminum Tube 3.0(OD)x0.095(WT) | 3 | 0.095 | 2.81 |
| 5052 SeamlessAluminum Tube 4.0(OD)x0.125(WT) | 4 | 0.125 | 3.75 |
| Fe | ≤ 0.4% |
| Si | ≤ 0.25% |
| Mn | ≤0.1% |
| Cr | 0.15~0.35% |
| Cu | ≤0.1% |
| Zn | ≤ 0.1% |
| Mg | 2.2~2.8% |
| other | Others 0.5% / Others total 0.15% |
| AL | Balance |
| Density | 2.68 |
| Melting Point | 605 – 650 |
| Elastic Modulus | 70 |
| Poisson’s Ratio | 0.33 |
| Thermal Conductivity | 138 |
| Thermal Expansion | 24.9 |
| Electrical Conductivity | 33 – 35 |
| Specific Heat Capacity | 0.900 |
| ASTM | ASTM B210, ASTM B241 |
| AMS (SAE) | AMS 4070, AMS 4071 |
| EN (Europe) | EN AW-5052 / EN 573-3 |
| JIS (Japan) | JIS H4000 / JIS H4080 |
| ISO | ISO 6361 |
| GB (China) | GB/T 3190, GB/T 4437.1 |